Carbon Graphite has the good property of good resistant-corrosion, high thermal conductivity and lower friction, good self-lubrication, and smaller expansion. They can be made into seal faces, bearings and so on. It is ideal to choose it as the frictional mating rings.
| Category | Model | Density (g/cm) | Fractural strength (Mpa) | Compressive Strength (Mpa) | Shaw Hardness | porosity | Temp (c) | |
|---|---|---|---|---|---|---|---|---|
| Carbon- Graphite | Hot Molded | M1 | 1.65 | 65 | 150 | 70 | 0.2 | 180 |
| Sintered carbon | MJ | 1.75 | 60 | 160 | 85 | 2.5 | 200 | |
| Impregnated Epoxy resin | M106H | 1.75 | 65 | 200 | 85 | 1 | 250 | |
| M120H | 1.70 | 60 | 180 | 80 | 1 | 250 | ||
| Impregnated Furan Resin | M106K | 1.75 | 67 | 200 | 90 | 1 | 250 | |
| M120K | 1.70 | 62 | 180 | 85 | 1 | 250 | ||
| Impregnated phenol Aldehyde M120F Tesin | M106F | 1.75 | 60 | 200 | 85 | 1 | 250 | |
| M120F | 1.70 | 55 | 180 | 80 | 1 | 250 | ||
| Antimony carbon | M106D | 2.30 | 65 | 220 | 90 | 1.5 | 400 | |
| M120D | 2.30 | 60 | 220 | 90 | 1.5 | 400 | ||
| M254D | 2.30 | 55 | 210 | 65 | 1.5 | 400 | ||